Pre-alloyed metal powder 1000 Series
| Description | ||
|---|---|---|
| MP1100 Components: Fe Cu Theoretical Density: 8.16g/cm3 Sintering Temperature: 830˚C Bending strength: 1,350MPa Hardness: 98-102HRB Application: Added as a basic powder to lower costs. |  |  |
| MP1200 Components: Fe Cu Theoretical Density: 8.25g/cm3 Sintering Temperature: 780˚C Bending strength: 1,250MPa Hardness: 94-98HRB Application: Suitable for medium and high-grade iron-based diamond tools. |  |  |
| MP1300 Components: Fe Cu Ni Theoretical Density: 8.23g/cm3 Sintering Temperature: 850˚C Bending strength: 1,400MPa Hardness: 108-112HRB Application: Medium diameter saw blades with high wear resistance for cutting granite. Medium and high-grade saw blades for cutting concrete. |  |  |
| MP1500 Components: Fe Cu Theoretical Density: 8.00g/cm3 Sintering Temperature: 850˚C Bending strength: 1,000MPa Hardness: 88-95HRB Application: Iron-based diamond tools to reduce the use of carbonyl iron powder. |  |  |
| MP1600 Components: Cu Sn Theoretical Density: 8.67g/cm3 Application: Traditional copper tin alloy powder. Low oxygen content good liquidity and stable performance. |  |  |
| MP1700 Components: Cu Sn Theoretical Density: 8.00g/cm3 Application: To reduce cost of tool production. |  |  |